This composition is the latest generation of RPA technical rollers.
Its unique mineralogical composition constituted of a ceramic matrix of very high purity raw materials provides to this roller quality a high flexural strength without compromising the resistance to thermal shock.
It is recommended for the production of large format and high load tiles specially for technical porcelain tiles produced in wide loading kilns.
ROLLERS 1093 | ROLLERS 1099 - TAPERED ROLLERS | ROLLERS 1093-B | ROLLERS 1100 | |
MINERALOGICAL COMPOSITION | MULLITE | MULLITE | MULLITE | MULLITE |
ZIRCONIA | ZIRCONIA | ZIRCONIA | ZIRCONIA | |
Al203 + ZrO2 | 80% | 82% | 85% | 87% |
WATER ABSORPTION | 10% | 10% | 9% | 8% |
APPARENT DENSITY | 2,60g/cm3 | 2,60g/cm3 | 2,65g/cm3 | 2,75g/cm3 |
MODULUS OF RUPTURA AT 25??C | < 450 kgf/cm2 | < 450 kgf/cm2 | < 480 kgf/cm2 | < 440 kgf/cm2 |
THERMAL EXPANSION | 50 (10 -7 ºC-1) | 50 (10 -7 ºC-1) | 50 (10 -7 ºC-1) | 49 (10 -7 ºC-1) |
MAXIMUM WORKING TEMPERATURE | 1280°C | 1150°C | 1300°C | 1300°C |
THERMAL SHOCK RESISTANCE | Very Good | Very Good | Very Good | Very Good |
NOTE: The above data is for general information and is based on typical process values.
Variations may occur and Refrat??rios Paulista reserves the right to modify them without prior notice.